PEI 基础创新塑料(美国) 1010 物性认证数据表

性能项目测试条件测试方法数值/描述单位机械性能拉伸强度(引张强度)ASTM D638/ISO 52715200kg/cm²(MPa)[Lb/in2]拉伸模量ASTM D638/ISO 527kg/cm²(MPa)[Lb/in2]拉伸屈服伸长率(延伸率)ASTM D638/ISO 5277.0%拉伸断裂伸长率(延伸率)ASTM D638/ISO 52760.0%弯曲模量(弯曲弹性率)ASTM D790/ISO 17860.0kg/cm²(MPa)[Lb/in2]弯曲强度ASTM D790/ISO 17822000kg/cm²(MPa)[Lb/in2]洛氏硬度ASTM D785109IZOD 缺口冲击强度1/4" 23℃ASTM D256/ISO 1790.6kg·cm/cm(J/M)ft·lb/in1/4" -30℃ASTM D256/ISO 179kg·cm/cm(J/M)ft·lb/in1/8" 23℃ASTM D256/ISO 179kg·cm/cm(J/M)ft·lb/in1/8" -30℃ASTM D256/ISO 179kg·cm/cm(J/M)ft·lb/in物性性能比重（密度）ASTM D792/ISO 11831.27成型收缩率ASTM D955%熔融指数（流动系数）200℃/5kgASTM D1238/ISO 1133g/10min220℃/10kgASTM D1238/ISO 1133g/10min吸水率 23℃/24HASTM D570/ISO 620.250%热性能热变形温度退火ASTM D648/ISO 75405 66psi℃（℉）未退火ASTM D648/ISO 75℃（℉）维卡软化点ASTM D1525/ISO R306426℃（℉）燃烧性（率）UL94V-0线性膨胀系数ASTM D696/ISO 113593mm/mm.℃电气性能介电常数100HZASTM D150/IEC 602503.151MHZASTM D150/IEC 60250介电损耗100HZASTM D150/IEC 602501MHZASTM D150/IEC 60250体积电阻率ASTM D257/IEC 600931E17Ω.cm表面电阻率ASTM D257/IEC 60093Ω耐电弧性ASTM D495/IEC 60112加工条件干燥条件加工温度射嘴℃料筒前段℃料筒中段℃料筒后段℃熔体温度℃模具温度℃压力注塑压力Mpa保压压力Mpa背压Mpa螺杆转速pm其他备注颜色特性用途